Cw713r Rod, Cw721r Brass Bars, BS 2874/ JIS High Tensile Brass Rods Casting Manufacturers.
JIS 3250H and HT1/HT2 IS 320 High Tensile Brass Rods Suppliers
High Tensile Brass Rods
Cw713r Rod
Cw721r Brass Bars
Zinc and copper are alloyed to produce brass. The result of their chemistry yields in a highly corrosion resistant alloy. Besides copper and zinc, a High Tensile Brass Rods Manufacturer may use additional elements to alloy brass, thereby increasing its properties, namely its tensile strength. For instance, Cw713r Rod is a high tensile brass alloy. This particular metal has been alloyed with elements like aluminium, manganese and silicon.
The chemistry of this alloy ensures that the resultant JIS 3250H High Tensile Brass Rods Casting tends to be almost as hard as aluminium bronze. However, this alloy tends to be considerably easier to process. Along with achieving high tensile strength, the other important properties of the CW713R HT2 IS 320 High Tensile Brass Rods includes good resistance to corrosion, good wear resistance and machinability. CZ114 or as also referred to as Cw721r Brass Bars, includes alloying elements like aluminium, iron, and manganese. This unique alloying chemistry results in a duplex microstructure in JIS 3250H High Tensile Brass Rods.
Grade CZ114 is well suited for applications involving extraction. Hence, the use of this HT1 IS 320 High Tensile Brass Rods are more often than not seen in marine environments. Since the content of copper in these rods are relatively higher than zinc, the resistance to seawater is characteristically inherent in these components. Along with marine engineering, the BS 2874 High Tensile Brass Rods is in high demand in the oil and gas industry as well.
- Size: 6 to 60mm
- Thickness:0 274 mm to 6.35 mm
- Thickness:4 mm to 150 mm
- Standard & Material: BS:1001, HT12472, IS:320l, IS 320 HT1 or HT2, BS 2874 CZ114 or CZ115,JIS 3250H C6782 or C6783
HT 12472/ JIS 3250H HT/ HT IS 320/ HT BS 1001 High Tensile Brass Rods Suppliers.
| Condition | Size | T.S. MPa | EL% Min | T.S. MPa | EL% Min |
| As manufactured | All Size | 430 min | 20.00% | 460 min | 20.00% |
| Cold-worked & Stress | 10-40 | 480 min | 12.00% | 520 min | 12.00% |
| Relieved | 40 above | 500 min | 15.00% |
| Chemical Requirements | HT1 | HT2 | |||
| Copper | 56.0 – 60.0% | 56.0 – 61.0% | |||
| Lead | 0.20 to 1.50% | 0.50 to 1.50% | |||
| Iron | 0.20 to 1.25% | 0.20 to 1.50% | |||
| Tin | 0.20 to 1.0% | 1.0% max | |||
| Aluminum | 0.2% max | 0.30 to 2% | |||
| Manganese | 0.25 – 2.0% | 0.50-2.0% | |||
| Total Imp. | 0.50% max | 0.50% max | |||
| Zinc | Remainder | Remainder |